The influence of different talc contents on the thermal and mechanical properties of thermoplastic polyurethane/polypropylene (TPU/PP) blends was investigated. The compatibility and crystallinity of TPU/PP and TPU/PP/T blends were determined by differential scanning calorimetry (DSC). The DSC results indicated that the addition of PP in TPU/PP blends increased glass transition temperature (T_g), melting temperature (T_m) and crystallinity (_c). The addition of talc has decreased T_m and _c and increased T_g and crystallization temperature (T_c). The effect of talc content on T_g, T_m and _c was insignificant, while T_c content increased. The T_g of nonfilled and talc-filled blends increased suggesting that the TPU and PP are partially compatible. Thermogravimetric analysis (TGA) showed improved thermal stability of all investigated nonfilled and talc-filled TPU/PP blends in the nitrogen atmosphere. In the air atmosphere only talc-filled TPU/PP 80/20 blends show a higher thermal stability, while thermal stability decreased for TPU/PP 50/50 and increased insignificantly for TPU/PP 20/80 blends. DSC and TGA results showed improved thermal properties of talc-filled TPU/PP blends when compared with nonfilled blends. The mechanical properties of talc-filled TPU/PP 50/50 and 20/80 blends improved in terms of tensile strength and Young’s modulus, while elongation of break decreased with the addition of talc and as the talc content increased.